Aluminum-coated single-mode optical fibers

Al-coated fibers
Aluminum-coated single-mode optical fibers have all the benefits of optical fibers include increased mechanical strength and greater fatigue resistance compared to non-hermetic and polymer-clad fibers (PCS). Their transmittance covers a spectral range of 1500 to 1600 nm, and also remains stable in corrosive chemicals that normally react to silica glass.

FEATURES:
  • Excellent mechanical strength and flexibility compared to polymer coated fibers.
  • The temperature range is from -196C to +400C.
  • The metal coating can be soldered.

 

General Properties
Core diameter, µm Clad diameter, µm Coating diameter, µm Cladding offset, % Coating offset, %
6.8 ± 0.5 125 ± 1 160 ± 5 < 2 < 5

 

General Properties
Core diameter, µm Clad diameter, µm Coating diameter, µm Cladding offset, % Coating offset, %
6.8 ± 0.5 125 ± 1 160 ± 5 < 2 < 5

 

General Properties
Core diameter, µm Clad diameter, µm Coating diameter, µm Cladding offset, % Coating offset, %
6.8 ± 0.5 125 ± 1 160 ± 5 < 2 < 5

 

Optical Properties
∆ n Core material Cutoff wavelength, nm Wavelength range, nm Mode field diameter (Gauss), µm Attenuation at 1550 nm1 C, dB/km
0.009 ± 0.001 Silica Ge-doped < 1450 1500 - 1600 7.5 ± 0.6 < 7.0

 

Optical Properties
∆ n Core material Cutoff wavelength, nm Wavelength range, nm Mode field diameter (Gauss), µm Attenuation at 1550 nm1 C, dB/km
0.009 ± 0.001 Silica Ge-doped < 1450 1500 - 1600 7.5 ± 0.6 < 7.0

 

Optical Properties
∆ n Core material Cutoff wavelength, nm Wavelength range, nm Mode field diameter (Gauss), µm Attenuation at 1550 nm1 C, dB/km
0.009 ± 0.001 Silica Ge-doped < 1450 1500 - 1600 7.5 ± 0.6 < 7.0

 

Operating conditions
Proof test, kpsi Min operating temperature,2,3 C Max operating temperature,2 C Short-term bending radius,mm Long-term bending radius,mm
100 -196 400 ≥ 10 ≥ 25

 

Operating conditions
Proof test, kpsi Min operating temperature,2,3 C Max operating temperature,2 C Short-term bending radius, mm Long-term bending radius, mm
100 -196 400 ≥ 10 ≥ 25

 

Operating conditions
Proof test, kpsi Min operating temperature,2,3 C Max operating temperature,2 C Short-term bending radius, mm Long-term bending radius, mm
100 -196 400 ≥ 10 ≥ 25
1- under normal climatic conditions
2- in inert environment
3- at the minimum operating temperature, the integrity of the optical fiber is guaranteed