Copper-coated single-mode optical fibers

Copper-coated single-mode optical fibers
Copper-coated single mode fibers are high strength optical fibers that can be used for both high-temperature and cryogenic applications. Thin additional carbon underlayer is typically added to improve hermetic property of the coating and therefore provide improved mechanical strength. This fiber type is used in sensor systems for biomedicine, oil and gas industry, aircraft applications, high vacuum devices, etc.

FEATURES:

  • Higher mechanical strength with respect to polymer coated fibers.
  • Solderable coating allows feeding the fibers into high vacuum systems and provides no outgassing.
  • The temperature range is from -196C to +600C.

 

General Properties
Core diameter, µm Clad diameter, µm Coating diameter, µm Cladding offset, % Coating offset, %
6.8 ± 0.5 125 ± 1 160 ± 5 < 2 < 5

 

General Properties
Core diameter, µm Clad diameter, µm Coating diameter, µm Cladding offset, % Coating offset, %
6.8 ± 0.5 125 ± 1 160 ± 5 < 2 < 5

 

General Properties
Core diameter, µm Clad diameter, µm Coating diameter, µm Cladding offset, % Coating offset, %
6.8 ± 0.5 125 ± 1 160 ± 5 < 2 < 5

 

Optical Properties
∆ n Core material Cutoff wavelength, nm Wavelength range, nm Mode field diameter (Gauss), µm Attenuation at 1550 nm1 C, dB/km
0.009 ± 0.001 Silica Ge-doped < 1450 1500 - 1600 7.5 ± 0.6 < 7.0

 

Optical Properties
∆ n Core material Cutoff wavelength, nm Wavelength range, nm Mode field diameter (Gauss), µm Attenuation at 1550 nm1 C, dB/km
0.009 ± 0.001 Silica Ge-doped < 1450 1500 - 1600 7.5 ± 0.6 < 7.0

 

Optical Properties
∆ n Core material Cutoff wavelength, nm Wavelength range, nm Mode field diameter (Gauss), µm Attenuation at 1550 nm1 C, dB/km
0.009 ± 0.001 Silica Ge-doped < 1450 1500 - 1600 7.5 ± 0.6 < 7.0

 

Operating conditions
Proof test, kpsi Min operating temperature2,3 C Short-term/Long-term bending radius,mm Max operating temperature (time < 60s)/(time > 60s)2C Permissible rate of temperature change in the temperature range, C/min
100 -196 ≥ 10/≥ 25 600/< 400 5

 

Operating conditions
Proof test, kpsi Min operating temperature2,3 C Short-term/Long-term bending radius,mm Max operating temperature(time < 60s)/(time > 60s)2 C Permissible rate of temperature change in the temperature range, C/min
100 -196 ≥ 10/≥ 25 600/< 400 5

 

Operating conditions
Proof test, kpsi Min operating temperature2,3 C Short-term bending radius, mm Max operating temperature(time < 60s)/(time > 60s)2 C Permissible rate of temperature change in the temperature range, C/min
100 -196 ≥ 10/≥ 25 600/< 400 5
1- under normal climatic conditions
2- in inert environment
3- at the minimum operating temperature, the integrity of the optical fiber is guaranteed